Lucas-Milhaupt Handy One 99088 AL 822 Flux Cored Brazing Rod, For Aluminum To Aluminum, Aluminum To Copper, Aluminum, Aluminum Alloys, Aluminum, Zinc, Lead, Cadmium, Other Elements, 0.09" Diameter, 20" Length, Flux Cored Finish, 800 °F (Solidus), 900 °F (Liquidus), 900-1000 °F (Brazing Range), 4 Pieces Container Size
Lucas-Milhaupt Handy One 99088 AL 822 Flux Cored Brazing Rod, For Aluminum To Aluminum, Aluminum To Copper, Aluminum, Aluminum Alloys, Aluminum, Zinc, Lead, Cadmium, Other Elements, 0.09" Diameter, 20" Length, Flux Cored Finish, 800 °F (Solidus), 900 °F (Liquidus), 900-1000 °F (Brazing Range), 4 Pieces Container Size
| Additional Information | : | Grayish White Color |
| Composition | : | Aluminum, Zinc, Lead, Cadmium, Other Elements |
| Container Size | : | 4 pieces |
| Container Type | : | Tube |
| Diameter | : | 0.09 " |
| Finish | : | Flux Cored |
| For Joining Material | : | Aluminum To Aluminum, Aluminum To Copper, Aluminum, Aluminum Alloys |
| Length | : | 20 " |
| Material Code | : | AL 822 |
| Series | : | Handy One |
| Shape | : | Rod |
| Temperature Rating | : | 800 °F (Solidus), 900 °F (Liquidus), 900-1000 °F (Brazing Range) |
AL 822 is a general purpose free flowing aluminum filler metal for joining of all brazeable grades of aluminum and aluminum alloys when using open air heating methods. This alloy is ideally suited for brazing of aluminum based HVAC/R coils and Cu lines and the repair of these units.Handy One is a proprietary family of brazing & soldering products that eliminates the need for a separate fluxing operation, which can result in a significant increase in productivity while minimizing flux exposure to your personnel and plant equipment.
Lucas-Milhaupt AL 822 Flux Cored Brazing Rod, Model: Handy One, For Aluminum To Aluminum, Aluminum To Copper, Aluminum, Aluminum Alloys, Aluminum, Zinc, Lead, Cadmium, Other Elements, 0.09" Diameter, 20" Length, Flux Cored Finish, 800 °F (Solidus), 900 °F (Liquidus), 900-1000 °F (Brazing Range), 4 Pieces Container Size, Tube, Rod
- Flux-cored design eliminates the need for separate flux application.
- Effectively joins aluminum to aluminum and aluminum to copper components.
- Low-temperature brazing with a solidus of 800°F and liquidus of 900°F.
- Creates high-strength joints, potentially exceeding 18,000 PSI shear strength with proper technique.
- Suitable for open-air heating methods in HVAC/R repairs and installations.
- Non-corrosive flux residue does not require removal after brazing.